[15p-A403-1~6] 17.1 カーボンナノチューブ，他のナノカーボン材料

▼ [15p-A403-4] Diameter-Dependent Photoluminescence Energy Observed in Color Centers of Air-Suspended Single-Walled Carbon Nanotubes

〇Daichi Kozawa¹、Xiaojian Wu²、Akihiro Ishii¹、Jacob Fortner²、Keigo Otsuka¹、Rong Xiang³、Taiki Inoue³、Shigeo Maruyama^3,4、YuHuang Wang²、Yuichiro K. Kato³ (1.RIKEN、2.Univ. Maryland、3.Univ. Tokyo、4.AIST)

キーワード：carbon nanotube, functionalization, color center

Color centers in single-walled carbon nanotubes attract interest because of their single-photon emission at room temperature in the telecom range [1, 2]. However, the lack of vapor-phase reaction route for forming color centers hinders the use of the excellent optical properties of air-suspended carbon nanotubes. We herein demonstrate the functionalization of air-suspended carbon nanotubes using iodobenzene as a precursor. The chemical reaction procedure is rationally designed to maintain the suspended structure and fluorescent properties of carbon nanotubes. The formed phenyl group serves as a color center and exhibits localized exciton emission peaks E₁₁^* and E₁₁^*- in addition to the free exciton emission peak E₁₁. We characterize over 12 different chiralities, covering nanotubes with diameters d ranging from 0.981 to 1.29 nm, to elucidate the reactivity and optical property of the color centers. We find that the reactivity of iodobenzene scales as 1/d, where the inherent strain on the curvature of nanotubes promotes the reaction. The trapping potential of E₁₁^* and E₁₁^*- are both close to the singlet-triplet splitting. The minimum value of g⁽²⁾(0) in the photon correlation verifies the photon antibunching at the color centers. These findings should lead to further development of quantum photon sources that utilize color centers in carbon nanotubes.