Convener:*Fumito Shiraishi(Department of Earth and Planetary Systems Science, Graduate School of Science, Hiroshima University), Tsubasa Otake(Division of Sustainable Resources Engineering, Faculty of Engineering, Hokkaido University), Yohey Suzuki(Graduate School of Science, The University of Tokyo), Ken Takai(Extremobiosphere Research Center, Japan Agency for Marine-Earth Science & Technology), Yuichiro Ueno(Department of Earth and Planetary Sciences, Tokyo Institute of Technology), Takeshi Naganuma(Graduate School of Biosphere Science), Takeshi Kakegawa(Graduate School of Science, Tohoku University), Tadashi Yokoyama(Department of Earth and Space Science, Graduate School of Science, Osaka University), Kentaro Nakamura(Precambrian Ecosystem Laboratory (PEL), Japan Agency for Marine-Earth Science and Technology (JAMSTEC))

6:15 PM - 7:30 PM

[BCG28-P01] Hydration and hardening prcess of iron and steel slags used for roadbed material

*Yu ARAI1, Tsubasa OTAKE2, Tsutomu SATO2 (1.Graduate school of engineering, Hokkaido University, 2.Division of Sustainable Resources Engineering, Faculty of Engineering, Hokkaido University)

Keywords:Slag, Hydration

Steel slag is a by-product of the steel manufacturing process and produced in large quantities every year. Steel slag is expected to reuse in Japan. However, it was observed that the uniaxial compressive strength (UCS) differs among mixed slag for roadbed materials produced from different factories including even with the same mixing ratio of DCS and GBFS. In particular, the difference between the UCS of slag produced from K ironworks and N ironworks was remarkable. The reason for these differences has not yet been clarified. To extend the market of steel slag, it is essential to clarify the relationship between secondary minerals formed after hydration and the UCS of the slag.
This study firstly investigated the UCS of the MIX slag ( DCS / GBFS = 4 ) from K ironworks and N ironworks. Based on the UCS tests, the slag from N ironworks is stronger than the slag from K ironworks.
Batch experiments were then conducted for samples from K ironworks and N ironworks to investigate and compare the evolution of solution chemistry and precipitation of secondary minerals during slag hydration. Based on the XRD analysis for the samples after the batch experiments, the main product of the MIX sample from K ironworks is αC2SH while the MIX sample from N ironworks produced mainly CSH. The difference in mineralogy could be related to the UCS of the slag because of the difference in volume of secondary minerals. Based on the solution analysis of the samples, it is observed that the main source of Ca ion is DCS, while the main source of Si ion is GBFS. In addition, it is possible that the concentration of H4SiO4 in the solution, which is present in the form of calcium silicate hydrates, is determined by GBFS. Kinetic model was constructed. The model represent the mineral evolution during slag hydration in the both MIX slags.