▼ [16a-421-9] Imaging of defects in zinc oxide by spectrally resolved two-photon fluorescence microscopy
Keywords:two-photon, Zinc Oxide, fluorescence
In this paper, we present a method for three-dimensional intrinsic defect imaging in zinc oxide (ZnO) by spectrally resolved two-photon fluorescence microscopy. Tightly focused light beam radiated by titanium-sapphire laser is used to obtain two-photon excitation of selected area of ZnO sample. Photoluminescence intensity of a specific spectral range is selected by optical band pass filters and measured by photomultiplier tube. Reconstruction of specimen image is done by scanning the volume of interest by piezoelectric positioning stage and measuring the spectrally resolved photoluminescence intensity at each point. The method was used to observe intrinsic defects in ZnO nanorods sample containing of nanparticles of length in range of 2.5-3.5μm and diameter in range of 0.3-0.5μm. Fig.1.c) shows undefected ZnO nanorods filtered at 390nm 1.d) oxygen vacancies V0 at 531nm and 1.e) zinc antisites OZn At 470nm. Spectral ranges were determined from measurements of fluorescence emission spectra and identified basing on literature [1][2].
Our method was proven to be effective in volume imaging of mechanical as well as intrinsic defects of ZnO. The resolution in x- and y-axis is estimated according to literature at 335nm and in z-axis at 1550nm. Method can be used for quality control of preprocessed semiconductors in search for mechanical impurities as well as determining the content of intrinsic defects at any stage of production of semiconductor devices. Other methods of volume defect identification, like XRD, provide information only about existence of various defects, without the ability to image them. Imaging of those defects will help in better understanding of their source and propagation, and might lead to significant improvements in suppressing the formation of impurities during processing of semiconductors.
Our method was proven to be effective in volume imaging of mechanical as well as intrinsic defects of ZnO. The resolution in x- and y-axis is estimated according to literature at 335nm and in z-axis at 1550nm. Method can be used for quality control of preprocessed semiconductors in search for mechanical impurities as well as determining the content of intrinsic defects at any stage of production of semiconductor devices. Other methods of volume defect identification, like XRD, provide information only about existence of various defects, without the ability to image them. Imaging of those defects will help in better understanding of their source and propagation, and might lead to significant improvements in suppressing the formation of impurities during processing of semiconductors.