[11p-Z08-18] Ionization ability of SiO2 containing NiFe2O4 nanoparticles modified with functional groups

Kota Aoki1, Yuma Sahasi2, Keita Kodama3, Kentaro Nashimoto3, Sota Hamada3, Yuko Ichiyanagi2,3,4 (1.Grad. Sch. of Environ and Info. Sci., Yokohama Nat. Univ., 2.Yokohama Nat. Univ., 3.Grad. Sch. of Sci. and Eng., Yokohama Nat. Univ., 4.Osaka Univ.)

Keywords:magnetic nanoparticles, mass spectrometry

SiO2包含NiFe2O4ナノ微粒子を作製し、さらに表面にアミノ基の修飾を行うことで、MS測定における粒径との関連並びに表面修飾によるイオン化支援機能の向上を目的とした。質量分析の結果、市販のDHBマトリクスに対し、我々の磁気ナノ微粒子を使用すると検出能力が向上した。中でも粒径が小さいもの、アミノ基を修飾した粒子が検出能力が高いため、吸光度測定と粒度分布測定を行うことでイオン化支援機能との相関を考察した。