[PY-30] セレン酸含有ソーダライトおよびカンクリナイトの安定性評価および各種生成条件での生成メカニズム考察
キーワード：TCLP試験、セレン酸含有ソーダライト、セレン酸含有カンクリナイト、水熱合成法
Matrix For Stable 79 Se Retention Is Desired To Be Developed For Long - Term Storage. Sodalite (Na (6 Tasu 2 Y Tasu Z) (AlSiO 4 ) 6 (X) (Y) (OH) Z .NH 2 O) And Cancrinite Na (6 + 2y + z) (AlSiO 4 ) 6 (X) (y) (OH) z .nH 2 O) can be efficient matrix for selenate (SeO 4 2 - Thus, in the present work work, the chemical stability of selenate-bearing sodalite and selenate-bearing cancrinite were investigated as Well As The Factors Affecting To The Formation Process.
TCLP Test Was Performed On The Solid Products To Evaluate Their Chemical Stability. It Was Revealed That The Solid Products Which Contain Very Low Weight Percent Of Cancrinite Showed Highest Chemical Stability. The Increase Of Cancrinite Weight Percent directly affected the chemical stability. not supported by XRD which are showing a decrease in d 300 cancrinite peak intensity after TCLP test. SEM images also selenate-bearing sodalite after TCLP test was recorded as low as 1.2 ppm which are 71 times lower than selenate-bearing cancrinite (85.1 ppm). Meanwhile, These more than one borderline temperature, with an increase in the initial selenate concentration, the crystallized phase, immobilized selenate, changed from sodalite to cancrinite. These results indicated the hydrothermal temperature and the initial doped selenate affect the matrix phase to accommodate selenate.
TCLP Test Was Performed On The Solid Products To Evaluate Their Chemical Stability. It Was Revealed That The Solid Products Which Contain Very Low Weight Percent Of Cancrinite Showed Highest Chemical Stability. The Increase Of Cancrinite Weight Percent directly affected the chemical stability. not supported by XRD which are showing a decrease in d 300 cancrinite peak intensity after TCLP test. SEM images also selenate-bearing sodalite after TCLP test was recorded as low as 1.2 ppm which are 71 times lower than selenate-bearing cancrinite (85.1 ppm). Meanwhile, These more than one borderline temperature, with an increase in the initial selenate concentration, the crystallized phase, immobilized selenate, changed from sodalite to cancrinite. These results indicated the hydrothermal temperature and the initial doped selenate affect the matrix phase to accommodate selenate.
講演PDFファイルダウンロードパスワード認証
講演集に収録された講演PDFファイルのダウンロードにはパスワードが必要です。
現在有効なパスワードは、［資源・素材学会会員専用パスワード］です。
※［資源・素材学会会員専用パスワード］は【会員マイページ】にてご確認ください。（毎年１月に変更いたします。）
［資源・素材学会会員専用パスワード］を入力してください