[177] Effect of Fe on Corrosion Behavior of Ni20Cr-xFe Alloys in Air with NaCl-KCl-CaCl2 Vapor at 570 °C
キーワード:High Temperature Corrosion、Oxidizing Chlorine Atmosphere、Ni-Cr Alloy、Effect of Iron、KCl-NaCl-CaCl2 Vapor
Corrosion kinetics decreased with addition of Fe. Fe oxide was found to form above the Cr2O3 scale, which might minimize the chromate formation.