Separation technology

[1E05-08] Separation technology

Thu. Nov 11, 2021 10:30 AM - 11:30 AM Room-E (Stadio-A/Hakodate Areana)

Chair:Shuhei Ogo(Kochi Univ.)

10:30 AM - 10:45 AM

[1E05] Separation of high pressure organic liquid through zeolite membranes

○Mikihiro Nomura1, Kazuki Kamata1, Masahide Matsuoka1, Katsunori Ishii1 (1. Shibaura Institute of Technology)

Polymeric membranes have been used as reverse osmosis membranes. In recent years, attention has been paid to inorganic membranes having excellent chemical resistance and pressure resistance. However, organic liquid permeation separation through a zeolite membrane has not been studied. Therefore, the purpose of this research is to develop an MFI zeolite membrane for high-pressure liquid permeation. Liquid separation of MFI zeolite membranes was investigated by performing ionic solution and organic solvent liquid permeation tests.

10:45 AM - 11:00 AM

[1E06] Synthesis of ethyl acetate by membrane reactor using AEI-type zeolite membrane

○Yuma Sekine1, Motomu Sakai2, Masahiko Matsukata1,2,3 (1. Department of Applied Chemistry, Waseda University, 2. Research Organization for Nano & Life Innovation, Waseda University, 3. Advanced Research Institute for Science and Engineering, Waseda University)

酢酸エチルは溶剤や高分子材料として利用される。エステル化は可逆反応であるため、エタノールと酢酸から酢酸エチルを合成する場合、収率は熱力学的平衡制約を受ける。ここで酢酸エチル収率を向上させるために、膜反応器の導入を検討した。膜として高い水透過度と選択性、耐酸性をもつAEI型ゼオライト膜を採用し、反応系からの脱水率が酢酸エチル収率に与える影響について検討し、シミュレーション結果との比較を行った。

11:00 AM - 11:15 AM

[1E07] Development of MIL-96 monolith for CO2 adsorption and desorption

○Hayata Hori1, Motomu Sakai2, Takaya Matsumoto3, Tsuyoshi Asano3, Masahiko Matsukata1,2,4 (1. Department of Applied Chemistry, Waseda University, 2. Research Organization for Nano & Life Innovation, Waseda University, 3. ENEOS Corporation, 4. Advanced Research Institute for Science and Engineering, Waseda University)

炭素循環型社会の実現に向けてCO2吸着材の開発が必要とされており、その材料として金属と有機配位子で構成される金属有機構造体(Metal-organic framework, MOF)が注目されている。しかし、MOFは主に粉末であり、吸着材として用いるためには賦形化技術の開発が必須である。本研究では、あらかじめ形を持った金属酸化物モノリスを直接MOFへ転換する手法を提案し、合成条件の検討を行った。

11:15 AM - 11:30 AM

[1E08] Investigation of dehydration performance from products of Fischer-Tropsch synthesis by ZSM-5 membrane

○Naoto Chihara1, Motomu Sakai2, Masahiko Matsukata1,2,3 (1. Department of Applied Chemistry, Waseda University, 2. Research Organization for Nano & Life Innovation, Waseda University, 3. Advanced Research Institute for Science and Engineering, Waseda University)

燃料製造技術であるFischer-Tropsch(FT)合成では、炭化水素だけでなく多量の水が副生する。この水は、原料分圧の低下や触媒の酸化・劣化の原因となることが知られている。これらの水による負の影響を低減するため、ゼオライト膜による、FT合成生成物からの気体状態での脱水について検討した。Fe系触媒を用いたFT合成（260 ℃, 0.9 MPa, H2/CO = 2/1）の生成物に対して、Na-ZSM-5膜を用いてH2Oの透過分離試験を行った。
×